ABSTRACT

Mold lens glass including B 2 O 3 , SiO 2 , La 2 O 3 , ZnO, BaO, and CaO, wherein a composition in weight ratio is: B 2 O 3  is 25% to 35% by weight, SiO 2  is 1% to 7% by weight, where a total amount of B 2 O 3  and SiO 2  is 30% to 40% by weight. A content of La 2 O 3  is 12% to 20% by weight, and a total amount of ZnO, BaO and CaO is 40% to 55% by weight. By using the mold lens glass of the present invention, it is possible to obtain mold lens glass having high refractive index, excellent water resistance and a stable glassy state.

TECHNICAL FIELD

[0001] The present invention relates to a glass composition for a lens which can be molded by hot pressing of glass preform between metal molds with curved surfaces of a lens, particularly to glass for mold lens having high refractive index and low dispersion.

BACKGROUND ART

[0002] Conventionally, a composition of optical glass has been determined to obtain necessary characteristics such as refractive index, Abbe's number, and chemical durability, without taking into account the lowering of glass transition temperature (Tg).

[0003] On the other hand, hot press molding technologies for a mold lens have been developed since around 1983, which requires no polishing and is capable of accurate control of a surface shape and surface roughness equivalent to those of a polished surface.

[0004] Glass for such mold lens is used for a pickup lens of an optical disk apparatus at present.

[0005] A mold lens can be obtained by pressing for a long time (about 20 sec.) at a temperature 10 to 20° C. higher than a flexure temperature of glass, using accurately ground and polished metal molds.

[0006] The metal mold surface is coated with a thin film of diamond-like carbon (DLC) or TiCN in order to release the mold lens from the metal molds.

[0007] The glass used for mold lens glass is required to be low in Tg for prolonging the life of the mold coating and reducing the cost, while it is desirable to be high in refractive index to reduce aberration of lens such as spherical aberration. That is, mold lens glass is required to be low in Tg and high in refractive index (n_(d)).

[0008] Further, in a case of glass which is easily crystallized, it is difficult to reliably produce an excellent lens, and therefore, a glass composition that hardly crystallizes is required.

[0009] Also, in a case of glass having poor water resistance, glass surface reacts with moisture in air, causing whitening of glass surface, and therefore, the water resistance of glass is required to be high enough.

[0010] The present invention is intended to provide mold lens glass having excellent water resistance, low Tg and high refractive index (n_(d)) and is hard to crystallize during a production process of glass.

DISCLOSURE OF THE INVENTION

[0011] Mold lens glass of the present invention includes B₂O₃, SiO₂, La₂O₃, ZnO, BaO, and CaO. A composition includes 25% to 35% by weight of B₂O₂ and 1% to 7% by weight of SiO₂. It includes 30% to 40% total weight of B₂O₃ and SiO_(2,) 12% to 20% by weight of La₂O₃, and 40% to 55% by total weight of ZnO, BaO and CaO.

DETAILED DESCRIPTION OF THE INVENTION

[0012] The mold lens glass (hereinafter referred to as “glass”) in the preferred embodiment of the present invention will be described in the following.

FIRST PREFERRED EMBODIMENT

[0013] Guaranteed grade reagents (JIS) of H₃BO₃, SiO₂, La₂O₃, ZnO, BaO and CaO were mixed to have a composition by which the present invention is characterized, and then mixture is melted at 1350° C. for 20 minutes.

[0014] Next, molten glass is poured onto metal molds previously heated up to glass transition temperature Tg and is vitrified.

[0015] Subsequently, glass thus obtained is cooled in an annealing furnace, at a cooling speed of 10° C./h from Tg to Tg−40° C. and, then, at 100° C./h to eliminate heat stress.

[0016] Next, the glass is formed into a rectangular parallel piped shape of 15 mm×15 mm×5 mm, and every surface are polished, followed by a measurement of refractive index and Abbe's number.

[0017] Further, a part of the glass is crushed into powder, and differential thermal analysis (DTA) is performed to obtain Tg, Ts, and liquid-phase temperature (T_(L)).

[0018] The vitrification ranges of glass thus obtained will be explained with reference to Table 1.

[0019] Glass compositions based on (SiO₂, B₂O₃)—La₂O₃ —(BaO, ZnO, CaO) and their characteristics are shown in Table 1.

[0020] Here, β values are calculated as parameters that show the stability of glass, that is, the extent of being hard to crystallize. The β values are calculated by the following equation, and the larger the value, the higher the stability of the glass.

β=(T _(c) −Tg)/(T _(L−T) _(c))

[0021] where Tg is glass transition temperature, T_(c), is crystallization temperature, and T_(L) is liquid-phase temperature.

[0022] Also, the refractive index, Abbe's number and characteristic temperature of each glass are measured.

[0023] Abbe's number vd is calculated by the following equation, and the larger the Abbe's number, the less the dispersion of the glass.

vd=(n _(d)−1)/(n _(F) −n _(c))

[0024] where n_(F) is refractive index at F line (wavelength 486.1 nm), n_(c) is refractive index at C line (wavelength 656.3 nm), and n_(d) is refractive index at d line (wavelength 587.6 nm).

[0025] Table 1 shows that the glass is unstable because the β value is as small as not more than 2 when the total amount of B₂O₃ and SiO₂, which is glass forming oxide, is about 25% by weight. Also, it is shown that Tg is very high when the total amount of B₂O₃ and SiO₂ exceeds 40% by weight, and is not suitable for mold lens glass.

[0026] Further, it is found that the stability of glass can be improved by mixing and substituting divalent metal oxide component (BaO) with other components (ZnO, CaO). TABLE 1 Tg T_(c) T_(L) No. B₂O₃ SiO₂ La₂O₃ BaO ZnO CaO (° C.) (° C.) (° C.) β n_(d) 1 30 — 15 55 — — 550 614 1029 0.154 — 2 30 — 20 50 — — 565 643 1023 0.205 — 3 30 — 25 45 — — 570 669 1023 0.280 — 4 35 — 10 55 — — 568 644 981 0.226 — 5 35 — 15 50 — — 577 670 979 0.301 1.671 6 35 — 20 45 — — 574 700 958 0.488 1.678 7 35 — 25 40 — — 593 747 941 0.794 1.686 8 40 — 10 50 — — 593 792 909 1.701 1.651 9 40 — 20 40 — — 599 737 873 1.015 1.673 10 40 — 30 30 — — 613 751 913 0.852 1.684 11 50 — 10 40 — — 600 820 923 2.136 1.627 12 50 — 40 10 — — 644 770 980 0.600 — 13 55 — 10 35 50 — 599 802 960 1.285 1.609 14 35 — 15 — 50 — 542 696 948 0.611 1.693 15 35 — 15 — — 50 Crystalized — — — — 16 35 — 15 40 10 — 560 796 852 4.214 1.680 17 35 — 15 30 20 — 547 740 803 3.063 1.685 18 35 — 15 20 30 — 541 798 837 6.590 1.689 19 35 — 15 10 40 — 534 693 867 0.914 1.692 20 30 — 20 — 50 — 536 648 822 0.644 1.717 21 30 — 25 — 45 — 534 664 861 0.660 1.725 22 25 10 15 20 30 — 554 711 823 1.402 1.689 23 20 15 15 20 30 — 558 836 940 2.673 1.689 24 30  5 15 20 20 10 552 810 906 2.688 1.689 25 25 10 15 20 20 10 557 805 889 2.952 1.689 26 20 15 15 20 20 10 556 732 819 2.023 1.689 27 21 15 15 20 20 10 570 740 793 3.208 1.687 28 15 10 15 24 24 12 532 772 1027 0.941 — 29 20  5 15 24 24 12 527 760 1012 0.925 — 30 15 15 15 22 22 11 540 812 921 2.495 1.692 31 20 10 15 22 22 11 532 803 916 2.398 1.701 32 25  5 15 22 22 11 528 795 910 2.322 1.713 33 25 15 15 18 18  9 623 853 928 3.067 1.678 34 30 10 15 18 18  9 614 827 901 2.878 1.686 35 35  5 15 18 18  9 601 802 876 2.716 1.691

SECOND PREFERRED EMBODIMENT

[0027] The second preferred embodiment of the present invention will be described in the following.

[0028] Glass is manufactured with the ratios of BaO, ZnO, and CaO varied where the glass compositions are set as B₂O₃=from 30% to 31% by weight, SiO₂=5% by weight, and La₂O₃=15% by weight.

[0029] The water resistance of glass obtained is measured by the following method. That is, glass powder equivalent to specific gravity (constant volume) and having particle diameter of from 250 μm to 420 μm is boiled one hour in boiling water, followed by a measurement of the decrease in weight (Dw) of the glass. The results are shown in Table 2. TABLE 2 No. B₂O₃ SiO₂ La₂O₃ BaO ZnO CaO n_(d) Dw (%) 1 30 5 15 20 20 10 1.689 0.532 2 30 5 18 18.8 18.8 9.4 1.696 0.316 3 30 5 17 19.2 19.2 9.6 1.701 0.439 4 32 5 15 19.2 19.2 9.6 1.695 0.361 5 31 5 17 18.8 18.8 9.4 1.691 0.478 6 31 5 15 14.7 29.4 4.9 1.689 0.038 7 31 5 15 9.8 29.4 9.8 1.687 0.014 8 31 5 15 4.9 34.3 9.8 1.691 0.055

[0030] As shown in Table 2, it is clear that the water resistance of the glass can be improved by optimizing the component ratio of divalent metal oxide.

INDUSTRIAL APPLICABILITY

[0031] As is apparent in the preferred embodiments of the present invention, the present invention is able to provide mold lens glass which has low Tg, high refractive index (n_(d)), is hard to crystallize during the production process, and has excellent water resistance. 

1. Mold lens glass including: 25% to 35% by weight of B₂O₃ and 1% to 7% by weight of SiO₂, a total amount of which being 30% to 40% by weight; and 12% to 20% by weight of La₂O₃, a total amount of ZnO, BaO and CaO being 40% to 55% by weight.
 2. The mold lens glass of claim 1, wherein weight ratios of said ZnO, BaO and CaO are; ZnO:BaO:CaO=25 to 35:5 to 16:4 to
 11. 